Translations between different materials standards

JUMU实名认证 发表于 2019-07-04 22:55 | 显示全部楼层 | 复制链接分享      上一主题  翻页  下一主题
Translations betweendifferent materials standards.
SS 14:   Swedishstandard is to be replaced by EN.
EN: European standards.
GB:       The people's republic of Chinastandards.
DIN:     DeutschIndustrie Norm Germany.
W.Nr:   Werkstoffnummer Germany.
AISI/SAE:   USA.

  ld-rolled sheet
  
SS 14
EN
GB
DIN
W.Nr
AISI/SAE
1142
DC01
?
St 12
  
St 13
  
St 14
1.0330
A366
  
A619
  
A620

  eneral structural  steel
  
SS 14
EN
GB
DIN
W.Nr
AISI/SAE
1312
S235JRG2
Q 235 A
  
Q 235 B
RSt 37-2
1.0038
  
(1.0116)
A570  Gr.36
1412
S275
?
St 44-2
1.0044
1020
1650
E335
?

1.0060

1672
C45E
45
  
45H
  
ZG310-570
C45E
  
Ck 45
1.1191
1045
2172
S355JR
Q 275
S355JR
1.0045
  
1.0050
1518

  icro alloyed  structural steel
  
SS 14
EN
GB
DIN
W.Nr
AISI/SAE
2132

?
20Mn5
1.1133
1022
  
1518
2134
S355N
16 Mn
StE 355
1.0545
  
1.0570


  eat treatment steel
  
SS 14
EN
GB
DIN
W.Nr
AISI/SAE
2225
25CrMo4
30CrMo
25CrMo4
1.7218
4130
2541
34CrNiMo6
?
34CrNiMo6
1.6582
4340

  ot work tool steel
  
SS 14
EN
GB
DIN
W.Nr
AISI/SAE
2242
X40CrMoV5-1
4Cr5MoSiV1

1.2344
H 13
Alloyed tool steel
SS 14
EN
GB
DIN
W.Nr
AISI/SAE
2260

Cr5Mo1V
X100CrMoV5-1
1.23633

2140

9CrWMn



2310

Cr12MoV
StE 355
1.2601



  Stainless steel
  
SS 14
EN
GB
DIN
W.Nr
AISI/SAE
2333
X5CrNi18-10
0Cr18Ni9
X 5 CrNi  18 10
1.4301
304

Observe that no quality should be castings.

  hemical composition
  
SS 14
C
  
%
Si
  
%
Mn
  
%
P
  
%
S
  
%
Cr
  
%
Mo
  
%
Ni
  
%
Cu
  
%
N
  
%
Others
  
%
1142
0,10
-
0,50
0,04
0,04
-
-
-
-
-
-
1312
≤0,20
0,25
0,4-0,7
0,050
0,050
-
-
-
-
≤0,009
-
1412
0,20
≤0,50
0,40-1,00
0,050
0,050
≤0,30
-
-
0,40
≤0,009
-
1650
0,38-,50
-
0,40-0,90
0,05
0,05
-
-
-
-
-
-
1672
0,42-0,50
0,10-0,40
0,80
0,035
0,035
-
-
-
-
-
-
2132
≤0,20
≤0,5
≤1,6
0,035
0,035
-
-
-
-
0,015
Nb  0,050
  
V  0,15
2134
≤0,20
≤0,5
≤1,6
0,035
0,035
-
-
-
-
0,015
Nb  0,050
  
V  0,15
2172
≤0,20
≤0,5
1,0-1,6
0,050
0,050
≤0,3
0,4
≤0,009
-
2225
0,22-0,29
0,10-0,40
0,60-0,90
0,035
0,035
0,90-1,20
0,15-0,30
-
-
-
-
2541
0,32-0,39
0,10-0,40
0,50-0,80
0,035
0,035
1,30-1,70
0,15-0,30
1,30-1,70
-
-
-
2242
0,35-0,42
0,80-1,20
0,30-0,60
0,030
0,020
5,00-5,50
1,20-1,60
-
-
-
V  0,85-1,15
2333
0,05
1,00
2,00
0,045
0,030
17,0-19,0
-
8,00-11,0
-
-
-
Mechanical propertiesSS 14 1312
Structuralstrength
  
SS-steel
  
Condition
Delivery form
Thickness of material
  
(mm)
ReL
  
(N/mm2)
  
≥
ReH
  
(N/mm2)
  
≥
Rm
  
(N/mm2)
  
A5
  
%
  
≥
Hardness
  
HB
1312-01
Normalized
Forged
≤  50
  
(50)-250
  
(250)-500
220
  
200
  
200
240
  
220
  
220
360-460
  
360-(460)
  
360-(460)
27
  
25
  
24
100-130
1312-03
Untreated or heat-treated
Seamless tube
≤  5
  
≥  5
240
  
220
260
  
240
360-490
24
-
1312-04
Untreated or heat-treated
Welded pipe
≤  5
  
>  5
240
  
220
260
  
240
360-490
24
-
1312-06
Cold worked
Bar
≤  50
370
-
≥ 440
10
(≥ 135)
1312-07
Cold worked
Seamless tube
≤  5
  
>  5
410
  
390
-
11


SS 14 2134
Structuralstrength
  
SS-steel
  
Condition
Delivery form
Thickness of material
  
(mm)
ReL
  
(N/mm2)
  
≥
ReH
  
(N/mm2)
  
≥
Rm
  
(N/mm2)
  
A5
  
%
  
≥
2134-01
Normalized
Forged
-16
  
(16)-35
  
(35)-50
  
(50)-70
350
  
340
  
330
  
320
360
  
350
  
340
  
330
470-630
20
2134-03
Normalized
Seamless tube
-16
  
(16)-20
350
  
340
360
  
350
470-630
20
2134-04
Normalized
Welded pipe
-16
  
(16)-20
350
  
340
360
  
350
470-630
20

SS 14 2134
Impactstrength
  
Thickness of material
  
(mm)
  
Test bar dimension
Temp
  
(oC)
  
KV
  
(J)
  
≥
6-(12)
  
12-70
5×10
  
10×10
-20
  
-20
18
  
27
SS 14 2172
Structuralstrength
  
SS-steel
  
Condition
Delivery form
Thickness of material
  
(mm)
ReL
  
(N/mm2)
  
≥
ReH
  
(N/mm2)
  
≥
Rm
  
(N/mm2)
  
A5
  
%
  
≥
Hardness
  
HB
2172-01
Normalized
Forged
-250
  
(250)-500
290
  
280
300
  
290
470-620
  
470-610
21
  
20
2172-03
Untreated or heat-treated
Seamless tube
≤  5
  
(5)-16
  
>  16
330
  
310
  
290
340
  
320
  
300
470-610
21
2172-04
Untreated or heat-treated
Welded pipe
≤  5
  
(5)-16
  
>  16
330
  
310
  
290
340
  
320
  
300
470-610
21
SS 14 2225
Structuralstrength
  
SS-steel
  
Condition
Delivery form
Thickness of material
  
(mm)
ReL
  
(N/mm2)
  
≥
ReH
  
(N/mm2)
  
≥
Rm
  
(N/mm2)
  
A5
  
%
  
≥
Hardness
  
HB
2225-03
Heat-treated
Bar
≤ 100
-
500
700-800
17
215-260



SS 14 2541
Structuralstrength
  
SS-steel
  
Condition
Delivery form
Thickness of material
  
(mm)
ReL
  
(N/mm2)
  
≥
ReH
  
(N/mm2)
  
≥
Rm
  
(N/mm2)
  
A5
  
%
  
≥
Hardness
  
HB
2541-03
Heat-treated
Bar
≤ 100
-
700
900-1100
12
275-335

SS 14 2333
Structuralstrength
  
SS-steel
  
Condition
Delivery form
Thickness of material
  
(mm)
Rp0,2
  
(N/mm2)
  
≥
Rm
  
(N/mm2)
  
A5
  
%
  
≥
Hardness
  
HB
2333-02
Solution heat treatment
Sheet,
  
Strip
-30
  
(30)-50
210
  
190
500
  
500
40
(200)
  
(200)
Solution heat treatment
Bar
-50
  
(50)-100
210
  
190
500
  
500
40
(200)
  
(200)
Solution heat treatment
Welded pipe
-10
  
(10)-
210
  
190
500
  
500
40
(200)
  
(200)



  
Heat treatable  aluminium alloy
  
SS
EN
GB
DIN
W.Nr
AA
4104
6063
?
AlMgSi0,5
3.3206
6063
4212-06
6082
?
AlMgSi1
2.2315
6082

  
Chemical composition
  
EN
Al
Si
Fe
Cu
Mn
Mg
Cr
Zn
Ti
6063
Residual
0,20-0,6
0,35
0,10
0,10
0,45-0,9
0,10
0,10
0,10
6082
Residual
0,7-1,3
0,50
0,10
0,40-1,0
0,6-1,2
0,25
0,20
0,10
EN AW-6082
Structuralstrength
  
Alloy
  
Delivery form
Condition
Thickness of material
  
(mm)
Rp0,2
  
(N/mm2)
  
≥
Rm
  
(N/mm2)
  
≥
A%
  
≥
A50%
  
≥
EN AW-6082
Extruded bar
O, H111
  
T4
  
T6
≤200
  
≤200
  
≤20
  
20
  
200
-
  
205
  
295
  
310
  
280
  
270
≤160
  
-
  
-
  
-
  
-
  
-
-
  
110
  
250
  
260
  
240
  
200
≤110
  
-
  
-
  
-
  
-
  
-
14
  
14
  
8
  
8
  
6
  
6
12
  
12
  
6
  
-
  
-
  
-
Extruded pipe
O, H111
  
T4
  
T6
≤25
  
≤25
  
≤5
  
5
-
  
205
  
290
  
310
≤160
  
-
  
-
  
-
-
  
110
  
250
  
260
≤110
  
-
  
-
  
-
14
  
14
  
8
  
10
12
  
12
  
6
  
8
Extruded sections
O, H111
  
T4
all
  
≤25
-
  
205
≤160
  
-
-
  
110
≤110
  
-
14
  
14
12
  
12
Open profile
  
T5
  
T6
≤25
  
≤25
  
≤5
  
5
  
270
  
290
  
310
-
  
-
  
-
  
-
  
230
  
250
  
260
  
-
  
-
  
-
  
8
  
8
  
10
  
6
  
6
  
8
Open profile
  
T5
  
T6
≤25
  
≤25
  
≤5
  
5
  
270
  
290
  
310
-
  
-
  
-
  
-
  
230
  
250
  
260
  
-
  
-
  
-
  
8
  
8
  
10
  
6
  
6
  
8


  ass
  
SS
EN
GB
DIN
W.Nr
ASTM
5170
CuZn39Pb3
?
CuZn39Pb3



  hemical composition
  
SS
Cu
  
%
Zn
  
%
Pb
  
%
5170
58
Residual
3

Structuralstrength
  
SS-steel
  
Rp0,2
  
(N/mm2)
  
≥
Rm
  
(N/mm2)
  
A5
  
%
  
≥
Hardness
  
HV
5170-00
  
-04
approx. 150
  
310-490
approx. 410
  
460-560
approx. 30
  
12-25
approx. 100
  
125-170

  ronze
  
SS
EN
GB
DIN
W.Nr
ASTM
5204-15

?ZcuSn5Pb5-Zn5
CuSn5ZnPb

UNSC83600


   hemical composition
  
SS
Cu
  
%
Sn
  
%
Zn
  
%
Pb
  
%
5204
85
5
5
5

Structuralstrength
  
SS-steel
  
Rp0,2
  
(N/mm2)
  
≥
Rm
  
(N/mm2)
  
A5
  
%
  
≥
Hardness
  
HB
5204-00
  
-03
  
-15
-
  
(90)
  
(100)
-
  
(230)
  
(250)
-
  
(15)
  
(13)
-
  
(60)
  
(70)

举报

返回列表
JUMU实名认证

关注0

粉丝14

图纸3482

推荐素材更多+

0

XY悬臂三条平面铝合金运动模组三维模型

  距米网  

找到您想要的设计

工程师、学生在线交流学习平台
关注我们

手机版- 距米网 |苏公网安备32041102000587号

©2017-2025 苏ICP备18040927号-1